【Key words】 Industrial pure nickel((Nickel 200)/Process qualification /Welding quality
Nikel 200 has excellent corrosion resistance in certain media, it is the best material for heat-resistant concentrated alkali solutions. It is also very resistant to neutral slightly acidic solutions and organic solvents. It has high strength and plasticity, especially in a cold and hot state, it has good processing performance. Therefore, pure nickel is often used in acid-base devices in the petrochemical industry to achieve anti-corrosion effects.
1. Nikel 200 ning payvandlash samaradorligini tahlil qilish
Sanoat sof nikelning tozaligi odatda 99 foizdan yuqori, jurnallarning massa ulushi 1 foizdan oshmaydi. Asosiy tuzilma ostenitik zanglamaydigan po'latga yaqin bo'lgan yuz-markazli kubik panjarali ostenitdir. Nisbiy zichlik misning zichligiga yaqin, u 8,9 g/ml.
Nikelning erish nuqtasi titanium va past karbonli po'latdan past, issiqlik o'tkazuvchanligi karbonli po'latdan past va elektr qarshiligi yuqori. Sof Ni payvandlari qotib qolganda fazali transformatsiyaga uchramaydi va ko'pincha qo'pol dendritik ostenit kristallarini hosil qiladi. Past erish nuqtasi bo'lgan aralashmalar S, P, Pb va boshqa elementlar don chegarasida past erish nuqtasi evtektikasini hosil qiladi, natijada termal yorilish paydo bo'ladi. Pure ni kichik qattiq{0}}suyuq faza harorat diapazoni va past suyuqlikka ega. H2, O2, CO2 va boshqa gazlarni suyuq holatda eritish oson. Bu gazlar o'z vaqtida chiqmasa, teshiklar hosil bo'ladi.
Bundan tashqari, yuqori qarshilik va past issiqlik o'tkazuvchanligi tufayli, payvandlash jarayonida ortiqcha qizib ketish oson, natijada payvand choklarining tez o'sishiga olib keladi, bu esa mexanik xususiyatlar va payvandlangan bo'g'inlarning korroziyaga chidamliligiga jiddiy ta'sir qiladi.
2. Payvandlash jarayonining malakasi
Welding procedure qualification is carried out in accordance with JB/T4756-2006 "Nickel and Nickel Alloy Pressure Vessels" and JB/T4745-2002 "Titanium Welding Vessels" Appendix B.
2.1 Payvandlash materiallari va sinov qismlarini tayyorlash
Jarayonning malakasi qo'lda volfram argonli payvandlashni (TIG) qabul qiladi, asosiy metall sanoat toza nikel (N6), payvandlashNikel 200 sim is ERNi-1 material of ф2.4mm, and the size of the test piece is 400mm300mm6mm. Compared with low alloy steel, pure ni welding has the characteristics of low permeability, but large line energy cannot be used to increase the permeability. The groove form should choose a large groove angle, the angle is 75 degree , the blunt edge is 1mm, Gap 2mm.
2.2 Tavsiya etilgan payvandlash jarayoni parametrlari
Past issiqlik o'tkazuvchanligi, oson qizib ketishi va payvand choklarining oson o'sishi bilan N6 ning xususiyatlarini hisobga olgan holda, payvandlash jarayonining parametrlarini, ayniqsa, chiziq energiyasini nazorat qilishni qat'iy nazorat qilish kerak. Amaliyot shuni ko'rsatdiki, faqat payvandlash oqimini kamaytirish usuli eng samarali emas, chunki suyuq nikel zaif suyuqlik va sayoz penetratsiyaga ega va haqiqiy oqim juda kichik bo'lmasligi kerak. Issiqlik kiritish payvandlash tezligini oshirish orqali boshqarilishi mumkin va qatlamlar orasidagi harorat payvandning birlashishini ta'minlash sharti bilan qat'iy nazorat qilinishi mumkin.
2.3 Sinov natijalari
Sinov qismi tugallangandan so'ng, 24 soat davomida xona haroratida joylashtirilgandan so'ng, payvand chokining sirtini tekshirish, RT-buzilmaydigan tekshirish va mikroskopik metallografik tekshirish amalga oshiriladi. Tekshiruv natijalari shuni ko'rsatdiki, payvandlangan joyda teshiklar mavjud, salbiyda esa yoriqlar topilmadi.
3 .Test natijalarini tahlil qilish
Sinov natijalaridan ko'rinib turibdiki, payvandlashda S va P aralashmalari juda kam bo'lganligi sababliNikel 200 sim, payvandlash jarayonida yuzaga keladigan past erituvchi evtektikalar soni- juda kam, shuning uchun issiq yoriq bo'lmaydi, chiziq energiyasi 10kJ/sm ichida boshqariladi va payvandlash paychalarining ichida Al va Ti qotishma elementlardir. donalarni tozalang va donning qo'pollashishi hodisasi yo'q.